III-V Materials
|
|
| Indium Phosphide |
| Orientation |
(100) |
|
Accuracy
|
±0.5° |
| Typical Diameter |
2" |
| Thickness |
0.45 -0.5mm |
| Dopant |
undoped |
| Epd |
< 5 x 10-2 x cm-2 |
| Flats |
according to standards |
| Polish |
epi |
|
| Gallium Phosphide |
| Orientation |
(100) |
|
Accuracy
|
±0.5° |
| Typical Diameter |
2" |
| Thickness |
0.35 - 0.4mm |
| Dopant |
P |
| Epd |
< 1 x 10-5 x cm-2 |
| Flats |
according to standards |
| Polish |
epi |
|
| Indium Antimonide |
| Orientation |
(100) |
|
Accuracy
|
±0.5° |
| Typical Diameter |
2" |
| Thickness |
0.45 -0.5mm |
| Dopant |
undoped |
| Epd |
< 5 x 102 x cm-2 |
| Flats |
according to standards |
| Polish |
epi |
|
| Gallium Antimonide |
| Orientation |
(100) |
|
Accuracy
|
±0.5° |
| Typical Diameter |
2" |
| Thickness |
0.45 -0.5mm |
| Dopant |
undoped |
| Epd |
< 1 x 10-2 x cm-2 |
| Flats |
according to standards |
| Polish |
epi |
|
| Indium Arsenide |
| Orientation |
(100) |
|
Accuracy
|
±0.5° |
| Typical Diameter |
2" |
| Thickness |
0.45 -0.5mm |
| Dopant |
N, P or undoped |
| Epd |
< 1 x 105 x cm-2 |
| Flats |
according to standards |
| Polish |
epi |
|
| Gallium Arsenide |
| Orientation |
(110) |
|
Accuracy
|
±0.5° |
| Typical Diameter |
2" |
| Thickness |
0.45 -0.5mm |
| Dopant |
undoped |
| Epd |
< 107 x Ohms cm |
| Flats |
according to standards |
| Polish |
epi |
|
| Gallium Arsenide |
| Orientation |
(111) |
|
Accuracy
|
±0.5° |
| Typical Diameter |
2" |
| Thickness |
0.45 -0.5mm |
| Dopant |
undoped |
| Epd |
< 107 x Ohms cm |
| Flats |
according to standards |
| Polish |
epi |
|
 |